VENOX SUPER ANTIFOULING BLACK LT. 0,75

Description

Antifouling paint formulated with a high content of coprous oxide and other antifouling agents. Particularly suitable in warm waters and in severe conditions. It’s antifouling power develops for a period over 12 months (for a film thickness of 100-120 dry microns). Recommended for work boats of wood, steel and fibreglass with a speed up to 30 knots.

 

SURFACE PREPARATION AND APPLICATION SYSTEM

Bare steel:

Apply 1 coat of EPOFOND AM-9 on sandblasted steel according to SA 2-2,5 and let dry for 12-24 hours. Apply then 2 coats of EPOFOND AM-9 allowing max.24 hours between coats (mimimum 6-8 hours). Overcoat then with 2 coats of VENOX SUPER antifouling , always allowing the required drying time between coats.

Bare wood:

Apply 1 coat of LIGNUM IMPREGNANTE followed by 2 coats of SOLVER PRIMER. Overcoat then with 2-3 coats of VENOX SUPER antifouling, always allowing the required drying time between coats.

Fiberglass (gelcoat ):

Apply 1 coat of UNIFIBER PRIMER followed by 2-3 coats of VENOX SUPER antifouling, always allowing the required drying time between coats.

Painted Hulls:

The bottom surface should be perfectly cleaned, free from fouling, rinsed with fresh water and sanded ( wet sandpapering is recommended, wear protective mask and googles during application to avoid contact with dust particles). Apply over the old antifouling (especially if the nature is unknown) 1 coat of SOLVER PRIMER as intermediate coat, followed by 2 coats of VENOX SUPER, always allowing the required drying time between coats.

 

Recommendations:

After the application of the last coat the maximum launching period of the antifouling is 1 month; with top quality copper based antifouling and after agreement with our technical staff, the launching time may extend up to 3 months, providing that the hull is protected from moisture, rain or atmospheric agents with plastic cover or similar material.

Color:

The color of the antifouling paint after immersion in water may result slightly different since small color. Differences can occur between different production lots: if necessary, mix them before application.

Remarks:

The values specified in the present technical data sheet may vary slightly from one batch to another. The antifouling paint must not come in contact with water, chemicals or subjected to mechanical stress before the curing is complete. The wet film thickness refers to the undiluted product In case of dilution, this value increases. The above information is the result of accurate laboratory tests and practical experience, however, since the product is predominantly used outside the manufacturer’s control, we can only guarantee the continuous quality of the product The above information may be subject to revision by our company For clarification, updates or further information, it is recommended to contact our company directly. LaThis technical data sheet cancels and replaces any other previously published data sheet.